Carboxylated styrene-butadiene rubber latex for shoe material |
Technological conditions:
Selecting the high quality comonomer and using scientific compatible method by emulsifier and additive, combined with outstanding craft to do emulsion polymerization. It is the active latex for sizing under leather making slurry in tannery industry.
Usage:
Applicable to internal sizing of fiber slurry, impregnating sizing with good fiber adsorptive capacity. Synthesis leatheroid has high peeling strength, and good wear resistance on surface.
Technical index;
|
No. |
6501(Soft glue) |
6802(Rigid glue) |
6903(Special hard) |
|
Middle bottom plate for shoes
(Applicable to wood fiber) |
Middle bottom plate for shoes
(Applicable to non-woven fabric) |
For shoes(Stiffener, heel)(Applicable to non-woven fabric) |
|
Solid content % |
48-50 |
48-50 |
48-50 |
|
PH value |
6-8 |
6-8 |
6-8 |
|
Viscosity mPa.s |
<200 |
<300 |
<100 |
|
Specific gravityg/cm3 |
0.98-0.99 |
0.98-0.99 |
0.98-0.99 |
Package, storage
Net weight: 200Kg. Plastic drum packaging. Storage temperature:5-40oC. Storage period: six months.
|
Carboxylated styrene-butadiene rubber latex for carpet |
Technology:
The product selects the high quality polymerization monomer (pyprolylene, styrene), emulsifier, chemistry additives and additive raw materials. Scientific compatible method uses domestic and foreign outstanding crafts to carry on emulsion polymerization of good chemical stability and mechanical stability.
Usage
It is designed for carpet backing adhesion which is suitable to needle-punched carpet, loop carpet and woollen carpet. With good compatibility of filler and high filling ratio to blend good stability of slurry.
Technical index:
| No. |
6414 |
|
Solid content % |
50±2 |
|
PH value |
6.5-8 |
|
Viscosity mPa.s |
<200 |
|
Diameter µm |
0.11-0.15 |
Package, storage
Net weight: 200Kg. Plastic drum packaging. Storage temperature:5-40oC. Storage period: six months.
|
Carboxylated styrene-butadiene rubber latex for papermaking |
Technological conditions:
The product uses the domestic advanced craft and technology and selects high quality copolymer monomer, emulsifier, chemistry additives and additive raw materials Scientific compatible method to carry on emulsion polymerization of good chemical stability and mechanical stability and small odour.
Usage:
It is special-purpose latex which designed for coating of papermaking industry. It forms relatively hard thin film on the paper and blends the paper coating which is good to paper’s adhesion with good whiteness, glossiness and smoothness. It is applicable to coating of art paper, manila board and glazed paper.
Technical index:
|
No. |
6391 |
6395 |
|
Solid content % |
50±2 |
50±2 |
|
PH value |
7-8 |
7-8 |
|
Viscosity mPa.s |
<200 |
<200 |
|
Diameter µm |
0.11-0.15 |
0.11-0.16 |
|
Glass temperatureoC |
14 |
13 |
Package, storage
Net weight: 200Kg. Plastic drum packaging. Storage temperature:5-20oC. Storage period: six months.
Carboxylated styrene-butadiene rubber latex for Leather
Technology:
Selecting the domestic and foreign high quality polymerization monomer (pyprolylene, styrene, carboxylic acid and so on), the emulsifier, chemical additives and other raw materials. Scientific method uses the domestic and foreign outstanding crafts to carry on the emulsion polyreaction. Good chemical stability and mechanical stability.
Usage:
Self-crosslinking, mixed with natural rubber latex to be stable propeller and make artifical leather perfect.
Technical index:
|
No. |
CSB–6601 |
|
Appearance |
Liquid of white with blue light |
|
Solid content % |
48±1 |
|
PH value |
7~9 |
|
Viscosity MPa.S |
< 200 |
|
Glass temperature oC |
3 |
Package, storage
Net weight: 200Kg. Plastic drum packaging. Storage temperature:5-40oC. Storage period: six months. | 